Co-Cr-Mo Alloy

A high-performance biocompatible material offering excellent wear and corrosion resistance, along with strong mechanical stability at high temperatures. It is ideal for dental restorations, dental frameworks, crowns, and trauma implants.

Request a quote

Description

Specifications

P-Physical property
Granule Diameter:	15-53 um
Shape:	Sphere
Flow ability:	40 S (Hall current meter)
Apparent density:	4.1 g/cm3
Tap density:	8.3 g/cm3

Chemical composition
Co:	Bal.
Cr:	26～30 wt%
Mo:	5～7 wt%
Si:	≤1 wt%
Mn:	≤1 wt%
Fe:	≤0.75 wt%
C:	≤0.16 wt%
Ni:	≤0.1 wt%

Performance of molded parts
Density:	≥99.9%
Rm Tensile Strength:	≥1100 MPa
Yield Strength:	≥900 MPa
Elongation:	≥10%
Elastic Modulus:	≥200 GPa
Hardness:	35～45 HRC (323～428 HB)